    mixed silicone rubberlocationindex>Product>mixed silicone rubber

    • High strength molded silicone
    • --introduce
    •  

      CharacteristicHigh transparency and high tear resistanceAbrasion resistance fatigue resistance and good compression set ; Harmless to the human body

      Applications: used for food grade, medical  products with special purposes that require high transparency and good strength

      Product after curing can be used between -50~250.

      Technical indicators:

      Pre vulcanization

      FST-7020

      FTS-7030

      FST-7040

      FST-7050

      FST-7060

      FST-7070

      FST-7080

      Surface

      Transparent

      Transparent

      Transparent

      Transparent

      Transparent

      Transparent

      Transparent

      Proportion

      1.050.02

      1.070.02

      1.130.02

      1.150.02

      1.180.02

      1.220.02

      1.260.02

      Curing ingredient

      C-8

      C-8

      C-8

      C-8

      C-8

      C-8

      C-8

      Standard dosage of vulcanizing agent

      1.5

      1.5

      1.5

      1.0

      1.0

      1.0

      1.0

      Post vulcanization                                        conditions of vulcanization1705min2mm

      Surface

      High transparency

      High transparency

      High transparency

      High transparency

      High transparency

      High transparency

      High transparency

      Line shrinkage

      3.4

      3.3

      3.2

      3.1

      3.0

      2.9

      2.8

      Solidity(HA)

      202

      302

      402

      502

      602

      702

      802

      Tensile strength(Mpa) 

      6.5

      8

      9

      8.5

      8.5

      8.5

      8

      Elongation at break(%)

      900

      850

      800

      700

      600

      500

      250

      Tension set(%)

      6

      5

      5

      5

      6

      8

      8

      Tearing strength(KN/M) 

      15

      20

      30

      40

      40

      40

      20

      Breakdown voltage KV/mm 

      22

      22

      22

      22

      22

      22

      22

      Volume resistivity

      110^14

      110^14

      110^14

      110^14

      110^14

      110^14

      110^14

      Flame resistance

      FV-1

      FV-1

      FV-1

      FV-1

      FV-1

      FV-1

      FV-1

      c-8: White paste  2,5-Dimethyl-2,5-di(tert-butylperoxy)hexane

       

      The main components of silicone rubber:methyl vinyl silicone rubber, hydrated silica, constitution controller, mold discharging agent

       

      This information is for reference only, if any doubt to the measured data shall prevail;

      Vulcanizing agent varieties, the amount of the actual production requirements to prevail;

      The vulcanization conditions are subject to the actual production requirements.